Polyolefin Compounds, Masterbatches and Elastomers

Consumer Goods Grade Summary 

Extron Grade Summary

Glass Fibre Reinforced Polypropylene

TYPICAL PROPERTIESGLASS FIBRE REINFORCEDCOUPLED GLASS FIBRE REINFORCED
 ASTM
Method
Unit
Specific GravityD792-1.051.131.041.121.221.271.35
Filler Level %20302030404550
Melt Flow IndexD1238
230°/2.16 kg
g/10 min22541.575
Mould Shrinkage** %0.2 - 0.80.2 - 0.70.2 - 0.80.2 - 0.70.1 - 0.40.1 - 0.40.1 - 0.4
Tensile StrengthD638MPa59697296116120125
Elongation at BreakD638%3233322
Flexural ModulusD790MPa39005800396059008500930011000
Izod Impact Strength
- notched
- unnotched
D256
D256
J/m
J/m
53
270
55
240
70
470
105
680
110
630
100
620
105
680
Hardness
-Durometer D
D2240
D2240
Inst
15 sec
79
72
80
75
77
72
83
77
86
79
84
78
84
80
Heat Deflection Temp
- 0.45 MPa
- 1.82 MPa
D648
D648
°C
°C
150
130
154
141
158
144
159
150
162
154
160
152
160
154
Co-efficient of Linear
Thermal Expansion
D696
-30 to 30°C
10-5per
°C
4343333

TYPICAL PROPERTIESImpact Mod.Glass & Mineral ReinforcedHigh GlossFood Contact
 ASTM
Method
Unit
Specific GravityD792-1.121.131.271.061.14
Filler Level %3030432330
Melt Flow IndexD1238
230°/2.16 kg
g/10 min589138
Mould Shrinkage** %0.2 - 0.70.2 - 0.80.2 - 0.70.2 - 0.80.2 - 0.7
Tensile StrengthD638MPa6380908850
Elongation at BreakD638%53222
Flexural ModulusD790MPa44504580772545006100
Izod Impact Strength
- notched
- unnotched
D256
D256
J/m
J/m
280
800
76
490
67
450
90
600
34
130
Hardness
-Durometer D
D2240
D2240
Inst
15 sec
76
67
81
74
82
76
81
76
80
75
Heat Deflection Temp
- 0.45 MPa
- 1.82 MPa
D648
D648
°C
°C
158
138
157
147
162
152
160
150
155
135
Co-efficient of Linear
Thermal Expansion
D69610-5per
°C
33343

Note: The above grade range is only an example of the grades / specifications available, so please contact us as for a more suitable material for your application.